The study of the influence of technological parameters of the impulse process on the formation of the weld metal and the microstructure of the heat-affected zone

Abstract

With prolonged operation of metal structures, the likelihood of their mechanical destruction increases. This also applies in many respects to the welded joints of main pipelines. One of the promising ways of solving the issue of increasing their service life is the development of welding methods based on the use of pulse control of process energy parameters. Pulse welding mode allows for controlled heat input into the welded joint zone, control of the electrode metal melting mode, formation of the weld metal structure and heat-affected zone (HAZ).Two types of metal transfer from the electrode to the weld pool were used in the work: with short circuits and without them, that is, welding was carried out on a "long" arc. At a constant electrode wire feed rate, the welding mode was changed by changing the shape of the current-voltage characteristic of the power source.

При тривалій експлуатації металевих конструкцій збільшується вірогідність їх механічного руйнування. Це значною мірою стосується і зварних з'єднань магістральних трубопроводів. Одним з перспективних шляхів розв’язання питання підвищення терміну їх експлуатації є розробка методів зварювання, заснованих на використанні імпульсного керування енергетичними параметрами процесу. Імпульсний режим зварювання дозволяє здійснювати регульоване тепловкладення в зону зварного з'єднання, керувати режимом плавлення електродного металу і формуванням структури металу шва та зони термічного впливу (ЗТВ). В роботі застосовувалося два види переносу металу з електроду в зварювальну ванну: з короткими замиканнями та без них, тобто виконувалось зварювання на "довгій" дузі. При постійній швидкості подачі електродного дроту режим зварювання змінювали шляхом зміни форми вольт-амперної характеристики джерела живлення.